无BPA(双酚A)PMMA, 无BPA(双酚A), 抗划伤性高, 耐紫外光, FDA 21 CFR 177.1010

 

PLEXIGLAS® V045

聚甲基丙烯酸甲酯-丙烯酸

 

Trinseo

 

Technical Data

 

产品说明

Plexiglas® V045 is a thermoplastic acrylic resin formulated for injection molding and extrusion applications. It is characterized by its chemical and heat resistance as well a high melt flow. Plexiglas® V045 has excellent weatherability and optical properties allowing it to excel in applications requiring outdoor stability, high quality surface appearance and/or precision optics. Plexiglas® V045 is easy to process due to its exceptional thermal stability, extrusion melt strength, and excellent tool surface reproduction and release properties. Supplemental moldflow simulation data is available. It has excellent resistance to many chemicals including solutions of inorganic acids, alkalis and aliphatic hydrocarbons such as VM&P naphtha and heptane. Additionally, it is virtually unaffected by a wide range of commercial products including many beverages, foodstuffs, detergent solutions and cleaners.

 

总览

材料状态 • 已商用：当前有效

资料 1 • Technical Datasheet

UL 黄卡 2 •  E39437-231434

• E39437-231435

搜索 UL 黄卡 •  Trinseo

•  PLEXIGLAS®

供货地区 • 北美洲

• 尺寸稳定性良好 • 耐热性，中等 • 收缩性低

特性 • 抗划伤性高 • 耐紫外光性能，良好

• 良好的颜色稳定性 • 清晰度，高 • 无 BPA

• 耐候性，良好 • 热稳定性，良好

用途 • 照明漫射器

机构评级 • FDA 21 CFR 177.1010

RoHS 合规性 • RoHS 合规

外观 • 半透明 • 可用颜色

• 不透明 • 清晰/透明

形式 • 粒子

加工方法 • 挤出 • 注射成型

 

物理性能 额定值(英制) 额定值(公制) 测试方法

密度 / 比重 1.19 1.19g/cm³ ASTM D792

熔流率（熔体流动速率） (230°C/3.8 kg) 2.3g/10 min 2.3g/10 min ASTM D1238

收缩率 - 流动 2.0E-3 到 6.0E-3in/in 0.20 到 0.60% ASTM D955

吸水率 (24 hr) 0.30% 0.30% ASTM D570

机械性能 额定值(英制) 额定值(公制) 测试方法

拉伸模量 450000psi 3100MPa ASTM D638

抗张强度 (断裂) 10200psi 70.3MPa ASTM D638

伸长率 (断裂) 6.0% 6.0% ASTM D638

弯曲模量 450000psi 3100MPa ASTM D790

弯曲强度 (断裂) 15000psi 103MPa ASTM D790

冲击性能 额定值(英制) 额定值(公制) 测试方法

悬壁梁缺口冲击强度 (73°F (23°C)) 0.30ft•lb/in 16J/m ASTM D256

硬度 额定值(英制) 额定值(公制) 测试方法

洛氏硬度 (M 级) 91 91 ASTM D785

热性能 额定值(英制) 额定值(公制) 测试方法

载荷下热变形温度 4 ASTM D648

66 psi (0.45 MPa), 已退火 202°F 94.4°C

264 psi (1.8 MPa), 已退火 199°F 92.8°C

维卡软化温度

-- 217°F 103°C ASTM D1525 5

-- 207°F 97.2°C ASTM D1525 6

导热系数 1.3Btu•in/hr/ft²/°F 0.19W/m/K ASTM C177

 

PLEXIGLAS® V045

聚甲基丙烯酸甲酯-丙烯酸

 

Trinseo

可燃性 额定值 (英制) 额定值(公制) 测试方法

UL 阻燃等级 HB HB UL 94

光学性能 额定值(英制) 额定值(公制) 测试方法

折射率 7 1.490 1.490 ASTM D542

透射率 (125.0 mil (3175 µm)) 92.0% 92.0% ASTM D1003

雾度 (125.0 mil (3175 µm)) < 1.00% < 1.00% ASTM D1003

补充信息 额定值(英制) 额定值(公制) 测试方法

ASTM Classification PMMA 0131V2 PMMA 0131V2 ASTM D788

注射 额定值(英制) 额定值(公制)

干燥温度 180 到 190°F 82 到 88°C

干燥时间 4.0hr 4.0hr

建议的最大水分含量 0.10% 0.10%

建议注射量 50% 50%

建议的最大回制料比例 20% 20%

料筒后部温度 420°F 216°C

料筒中部温度 430°F 221°C

料筒前部温度 440°F 227°C

射嘴温度 430°F 221°C

加工（熔体）温度 < 520°F < 271°C

模具温度 150 到 190°F 66 到 88°C

注射速度 快速 快速

背压 100psi 0.689MPa

螺杆转速 50 到 100rpm 50 到 100rpm

螺杆长径比 15.0:1.0 到 15.0:1.0 到

20.0:1.0 20.0:1.0

螺杆压缩比 2.0:1.0 至 2.5:1.0 2.0:1.0 至 2.5:1.0

排气孔深度 2.0E-3in 0.051mm

 

 

 